AURAPENE PPTF30BK
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Aurora Manufacturing Ltd |
| Trademark: | AURAPENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XWrFEg_AURAPENE-PPTF30BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPTF300BK is a general purpose 30% talc filled polypropylene compound with good UV performance, manufactured from recycled polymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 to 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | > 5.2 | kJ/m² | ISO 179/B |
| Notched Izod Impact Strength | > 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Rear Temperature | 195 to 230 | °C | |
| Middle Temperature | 195 to 230 | °C | |
| Front Temperature | 195 to 230 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4011 | RTP Company | PPA | RTP |
| ALKAMIX™ MB-AF220 | Marplex Australia Pty. Ltd. | Unspecified | ALKAMIX™ |
| Cheng Yu FV3050 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| KMI PP KM-001JB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| TECACOMP® PEEK 450 MT CF30 black 3569 | Ensinger GmbH | PEEK | TECACOMP® |