NYCOA NanoSEAL™ NS-8330 UV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA NanoSEAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XWkgbp_NYCOA-NanoSEAL-NS-8330-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA nanoSEAL™ NS - 8330 UV is a proprietary clay based Nanocomposite made via in-situ polymerization for optimum nano-clay exfoliation. The grade exhibits a higher degree of stiffness and superior toughness compared to standard impact modified Nylons. NYCOA nanoSEAL™ NS - 8330 UV has been specifically formulated for extrusion, blow-molding, and injection molding applications. This grade offers a 55% improvement in barrier properties over traditional Super-Tough Nylons. In addition, this product is UV stabilized for prolonged outdoor exposure to sunlight. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 60.0 | MPa | ASTM D638 |
| Tensile Elongation 1(Break) | 25 | % | ASTM D638 |
| Flexural Modulus 2 | 2210 | MPa | ASTM D790 |
| Flexural Strength 3 | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | No fracture 800 J/m | ASTM D256 | |
| Unnotched Izod Impact (6.35 mm) | No fracture 1900 J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 238 - 249 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 249 - 266 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 65.6 - 76.7 | °C | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® SMC 1000 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Moplen RP241R | LyondellBasell Industries | PP Random Copolymer | Moplen |
| EVATHENE® UE659 | USI Corporation | EVA | EVATHENE® |
| Keysor PVC KC1501-835 Natural | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| MACOMASS PP MM-PP HE 52 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |