Ecomass® 706BI76
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Ecomass Technologies |
| Trademark: | Ecomass® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XVgZuG_Ecomass-706BI76.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ecomass® 706BI76 is an Acrylonitrile Butadiene Styrene (ABS) material filled with filler. It is available in North America for injection molding. Primary attribute of Ecomass® 706BI76: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage (4.00 mm) | 0.30 to 0.50 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 to 5.0 | % | ISO 527-2 |
| Flexural Modulus | 5470 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 64 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 84.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 82.2 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Processing (Melt) Temp | 204 to 246 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Injection Pressure | 68.9 to 103 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 to 0.172 | MPa | |
| Screw Speed | 100 to 250 | rpm | |
| Clamp Tonnage | 3.4 to 5.5 | kN/cm² | |
| Cushion | 6.35 to 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titanvene™ HD5301AA | PT. TITAN Petrokimia Nusantara | HDPE | Titanvene™ |
| Xuchuan XCW-6650D | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Akulon® K224-HG7 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| DEXFLEX® 711 | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| PEARLCOAT® Activa D118K | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLCOAT® |