CERTENE™ HI-960
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XVWy3y_CERTENE-HI-960.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HI-960 is a certified prime homopolymer designed for molding applications requiring high warpage resistance and good balance of mechanical properties. HI-960 features easy processability, very good stiffness, good impact strength, high surface gloss, and excellent dimensional stability. HI-960 applications include crates, waste bins, pails, housewares, tote bins, fruit and vegetable trays, and structural foam. HI-960 recommended processing temperature is 210 to 240°C. with mmold @ 20 to 40°C.. HI-960 is not UV stabilized. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, Compression Molded, F50) | 5.00 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 29.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 1000 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Compression Molded) | 1520 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 60.9 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79.0 | °C | ASTM D648 |
| Brittleness Temperature | -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH308G50 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| TEKNIFLEX® VPOA10200 ALU | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| TOTAL Polypropylene PPC 4481WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Dynaflex™ G7930-9001-02 | PolyOne Corporation | TPE | Dynaflex™ |
| TECACOMP® PA66 TC black 4028 | Ensinger GmbH | Nylon 66 | TECACOMP® |