Order Products : sales@su-jiao.com
Badamid® LB70 S
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XUipcP_Badamid-LB70-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LB70 S is a Polyamide 6 (Nylon 6) material. It is available in Europe. Primary attribute of Badamid® LB70 S: Flame Rated. |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 to 3.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3400 | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 90.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 10 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 4.0 | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 5.0 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 220 | -- | °C | ISO 3146 |
| CLTE - Flow | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 60216 | |||
| -- 2 | 87 | -- | °C | |
| -- | 180 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.30 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| 2 . | 20000 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx P65E0 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| Sanren F280 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Spartech Polycom SC8F-2088 | Spartech Polycom | PPE+PS | Spartech |
| TOPAS® 6013L-17 | Polyplastics Co., Ltd. | COC | TOPAS® |
| TECACOMP® PET TRM black 9415 | Ensinger GmbH | PET | TECACOMP® |