TAIRILOY AC2000
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRILOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XTkpSl_TAIRILOY-AC2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC PC/ABS resin AC2000 meets the requirements of UL, SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 | g/cm³ | ASTM D792 |
| 23°C | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class R, 23°C | 112 | ASTM D785 | |
| R scale, 23°C | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 53.9 | MPa | ASTM D638 |
| 23°C | 54.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2450 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 89.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 3.18 mm) | 590 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 106 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Die Temperature: 230 to 270°CInjection Volume: 30 to 80% of injection machine's capacity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND DF - Ix Series | POLY GIN | PC | MARCOBLEND |
| TEKNIFLEX® VPA780 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| Leona™ 1700S | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LNP™ LUBRICOMP™ EX03599H compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| OTECH PVC OW930 - A/V Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |