SABIC® PPcompound 9712
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XTYMeO_SABIC-PPcompound-9712.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 9712 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV stability. This material can exhibit ductility at temperatures as low as -30 degrees C. The IMDS is 164207488. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| -- | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 22.0 | MPa | ISO 527-2/50 |
| Break | 15.7 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | |
| Break | 65 | % | |
| Flexural Modulus 1(64.0 mm Span) | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 3.1 | kJ/m² | |
| 23°C 3 | 34 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 4.5 | kJ/m² | |
| 23°C | 33 | kJ/m² | |
| Instrumented Dart Impact 5 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 22.9 | J | |
| 23°C, Energy at Peak Load | 19.3 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 136 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 58.0 | µm/Mk | |
| Transverse : -30 to 100°C | 150 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4mm, Cut |
| 3 . | 80*10*4 mm, Cut |
| 4 . | 80*10*4mm, Cut |
| 5 . | 6.60 m/sec |
| 6 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6045E BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALTECH® PP-H A 2030/652 GF30 UV CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| INSULCAST® 101 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| KARINTOX 70/2 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | KARINTOX |
| LUVOCOM® 1105-8000 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |