LNP™ THERMOCOMP™ JX97000 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XTLEUP_LNP-THERMOCOMP-JX97000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JX97000 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release. Also known as: LNP* THERMOCOMP* Compound PDX-J-97000 Product reorder name: JX97000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 139 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8200 | MPa | ISO 178 |
| Flexural Stress | 183 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 224 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 218 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 325 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| TORZEN® U3501 NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| ELASTOSIL® AUX PRIMER G 3244 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| Geon™ Vinyl Flexible XV3796 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ESTOPLAST XU 400NN12 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |