3M™ Dyneon™ PTFE Compound NST 1111R

Category:	PTFE , Polytetrafluoroethylene
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ PTFE Compound
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XTFqEM_3MDyneonPTFECompoundNST1111R.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

3M™ Dyneon™ Compound NST 1111R is a free-flowing suspension PTFE compound containing 5% graphite and 10% of an appropriate filler for ram extrusion, compression and automatic moulding.

Special Features

Increased thermal dimensional stability

Increased surface hardness

Improved deformation under load

Reduced friction and wear

Good chemical stability

High limiting oxygen index (LOI)

Low friction behaviour

Very good mechanical properties

Exceptional temperature resistance

General Information
Filler / Reinforcement	Graphite fiber reinforced material, 5.0% filler by weight Filler, 10% filler by weight
Features	Low friction coefficient
Uses	Seals Application in Automobile Field
Forms	Powder
Processing Method	Compression molding Plunger press-out

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.17	g/cm³	ASTM D4745-06
Apparent Density	0.76	g/cm³	ASTM D4894-07
Molding Shrinkage - Flow	2.8	%	ASTM D4894-07

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	69		DIN 53505

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	19.5	MPa	ASTM D4745-06
Tensile Elongation (Break)	370	%	ASTM D4745-06

Resin Grade	Manufacturer	Category	Trademark
Sylvin 8954-92 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
TES J-4/30/V0 NAT	Techmer Engineered Solutions	Nylon 612	TES
UBESTA 3035 JU5	UBE Engineering Plastics, S.A.	Nylon 12	UBESTA
Zhongfa PBT G-20V	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PBT	Zhongfa
Devcon 1 Minute™ Epoxy Gel	Devcon	Epoxy	Devcon