NYLOY® MG-0034N-V0 B14
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XTE32b_NYLOY-MG-0034N-V0-B14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYLOY® MG-0034N-V0 B14 is a Polyamide 66 (Nylon 66) material filled with 34% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of NYLOY® MG-0034N-V0 B14 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.39 | % | |
| Across Flow | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 127 | MPa | ASTM D638 |
| -- | 123 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 9210 | MPa | ASTM D790 |
| -- | 9200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 184 | MPa | ASTM D790 |
| -- | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 68 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 230 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicostirolo 682V0 | Ravago Group | PS (HIPS) | Sicostirolo |
| Solef® 11010 | Solvay Specialty Polymers | PVDF | Solef® |
| Comco PA 6/12 G | Comco-Plastic GmbH | Nylon 6/12 | Comco |
| Lifoflex® GB 1060 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| Evoprene™ G 618 | Mexichem Specialty Compounds Inc. | TPE | Evoprene™ G |