Order Products : sales@su-jiao.com
Infino LS-1159S
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XSoeXq_InfinoLS1159S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino LS-1159S is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 220°C/10.0 kg | 25 | g/10 min | ASTM D1238, ISO 1133 |
| 250°C/2.16 kg | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.10 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.10 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.10 | % | ISO 2577 |
| Traffic : 3.20mm | 0.10 | % | ISO 2577 |
| Ash Content | |||
| -- | 14 | % | ASTM D5630 |
| -- | 14 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3900 | MPa | ASTM D638 |
| -- | 4000 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 88.0 | MPa | ASTM D638 |
| Yield | 90.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 88.0 | MPa | ASTM D638 |
| Fracture | 90.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 3.0 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 5 | |||
| -- | 4400 | MPa | ASTM D790 |
| -- | 4500 | MPa | ISO 178 |
| Flexural Strength 6 | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 79 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 79 | J/m | ASTM D256 |
| 23°C 8 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 93.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-1 | UL 94 | |
| 2.0 mm | V-0 | UL 94 | |
| 2.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4mm |
| 8 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8150C | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| XANTAR® 24 U | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ALCOM® PC 740/4 UV CC1269-08LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Gallonprene® GP520-5012 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| EPOXIDUR® EP 3582 | RASCHIG GmbH | Epoxy | EPOXIDUR® |