ENGAGE™ XLT 8677 Polyolefin Elastomer is an ethylene octene copolymer developed for use as a high efficiency impact modifier for thermoplastic polyolefin (TPO) applications. This product is delivered with a nominal talc partitioning agent to assist in material handling. Main Characteristics:
Applications
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.870 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 45 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, Compression Molded | 51 | ||
| Shore D, Compression Molded | 11 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 1.21 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 3.00 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | > 1000 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 6.55 | MPa | |
| 2% Secant : Compression Molded | 6.34 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 26.3 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -65.0 | °C | Internal Method |
| Melting Temperature (DSC) 4 | 118 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V932 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Staramide RB004 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Fainplast PVC PM 65 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| ADVANCENE™ bEE-4906-AAH | ETHYDCO | HDPE, HMW | ADVANCENE™ |
| Silastic® Medical Adhesive Silicone, Type A | Dow Corning Corporation | Silicone | Silastic® |