Ultraform® N 2200 G43
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XSV9fg_Ultraform-N-2200-G43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection molding grade for parts requiring high stiffness and strength together with good mold release. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Apparent Density | 0.85 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.3 | % | ISO 294-4 |
| Flow direction | 1.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.90 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 164 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Tensile Creep Modulus 1(1000 hr) | 4500 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.5 | kJ/m² | ISO 179/1eA |
| 23°C | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 161 | °C | ISO 75-2/A |
| Melting Temperature | 168 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Maximum operating temperature- short cycle operation | 110 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | FMVSS 302 | |
| ISO Type | POM-K, M-GNR, 02-003, GF20 | ISO 9988-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 85 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 200 | °C | |
| Rear Temperature | 205 | °C | |
| Middle Temperature | 205 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 60.0 - 120 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Note Message | |
|---|---|
| 1 . | strain <= 0,5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PA66 EN230 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |
| XYRON™ X304H | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Celanex® 3316 | Celanese Corporation | PBT | Celanex® |
| Karina BLACK PVC COMPOUND TR-602D48/ 1-Y-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ROTOLENE® Black Total Plus | Polimeros Mexicanos S.A. de C.V. | LMDPE | ROTOLENE® |