FLEXITEQ™ F50D010UV
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | FLEXITEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XRuegL_FLEXITEQ-F50D010UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLEXITEQ™ F50D010UV is a formulation based on Santoprene™ rubber technology. It features an optimal balance of processability, formability and material properties with enhanced heat and UV stability, and can be formulated in a pre-coloured material. FLEXITEQ™ F50D010UV can be processed on conventional thermoplastic equipment for injection moulding. It is polyolefin based and is completely recyclable. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 62 | ASTM D2240 | |
| Shaw D, 15 seconds | 51 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1(3.20 mm) | 405 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D412 | ||
| Yield | 16.2 | MPa | ASTM D412 |
| Fracture | 17.3 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 650 | % | ASTM D412 |
| Tear Strength 4 | 110 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 136 | °C | ASTM D1525 5 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 185 - 205 | °C | |
| Middle Temperature | 195 - 220 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Injection Pressure: High |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | C mold, 500 mm/min |
| 3 . | Mouth die C, 500 mm/min |
| 4 . | C mold, 500 mm/min |
| 5 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 TC-I-20 FR | RTP Company | PPS | RTP |
| Sindustris ABS LLG850W | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| DENISTAT N 35GC 03 | Vamp Tech | Nylon 6 | DENISTAT |
| Hanwha Total PP TB53L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina BROWN PVC COMPOUND 800-36/61-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |