PRL TP-FR-IM2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XRirBo_PRL-TP-FR-IM2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-FR-IM2 is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 to 1.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 37.9 | MPa | |
| Break, 3.18 mm | 37.9 | MPa | |
| Flexural Modulus (3.18 mm) | 2100 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 640 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 127 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 118 | °C | |
| RTI Elec | UL 746 | ||
| 0.750 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 246 to 274 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3024 LU | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| ACCUTECH™ HP0336W20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Karina CLEAR PVC COMPOUND -E 80/200-SI-CRMT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GREEN COLOR CONCENTRATE -E 40/272-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 916VO-90 Grey 9459 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |