Sarlink® TPE AB-2244N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XQvRev_Sarlink-TPE-AB-2244N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE AB-2244N is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ISO 2557 | ||
| Flow : 23°C, 48 hours, 2.00mm | 1.1 | % | ISO 2557 |
| Transverse flow : 23°C, 48 hours, 2.00mm | 1.1 | % | ISO 2557 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 44 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 2.00 mm) | 95.6 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C, 2.00 mm) | 214 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(100% strain, 23°C, 2.00mm) | 9.17 | MPa | ASTM D412 |
| Tensile Strength 3(Break, 23°C, 2.00 mm) | 20.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 690 | % | ASTM D412 |
| Tear Strength 4(23°C, 2.00 mm) | 87.6 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 47.0 | °C | ISO 75-2/B |
| Glass Transition Temperature | -55.0 | °C | DSC |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 62 | mm/min | FMVSS 302 |
| Fogging 5 | 96.0 | SAE J1756 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 227 - 243 | °C | |
| Nozzle Temperature | 232 - 249 | °C | |
| Processing (Melt) Temp | 232 - 249 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | 500 mm/min |
| 5 . | 3 hrs @ 100°C, 21°C Plate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LRS768L | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| CompaMid® PA 6.6 | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| Ferro PP NPP00GX12BK | Ferro Corporation | PP Copolymer | Ferro PP |
| Gallonprene® GP520-7511 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Plaslube® PA6 TX10 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |