ACLAR® 33C (0.75 mil)
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XQcsRR_ACLAR-33C-0-75-mil-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclar 33C (0.75 mil) is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is thermoformable on both pressure and vacuum forming machines. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.12 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 19 µm | 1660 | MPa | ASTM D882 |
| TD : 19 µm | 1450 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 19 µm | 83.0 | MPa | ASTM D882 |
| TD : Yield, 19 µm | 27.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 19 µm | 100 | % | ASTM D882 |
| TD : Yield, 19 µm | 100 | % | ASTM D882 |
| Water Vapor Transmission Rate (19 µm, 38°C, 100% RH) | 0.42 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 206 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (19.1 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 24.8 m²/kgTear Strength, ASTM D1004, Graves MD: 400 to 450 g/milTear Strength, ASTM D1004, Graves TD: 350 to 400 g/milCrystalline Melting Point, ASTM D4591: 206 °CDimensional Stability, ASTM D1204, MD: |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen H30S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| TEREZ PA 6 7851 T GF 30 H UV | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Braskem PP H 503 | Braskem | PP Homopolymer | Braskem PP |
| FERREX® GPP35CG40UL GRAY | Ferro Corporation | PP Homopolymer | FERREX® |
| Petrothene® NA362 | LyondellBasell Industries | LDPE | Petrothene® |