Starex BF-0679P
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XPrUkg_Starex-BF-0679P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Scratch resistant material that is used for the exterior material of flat TV |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 13 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.40 | % | |
| Across Flow : 3.20 mm | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 116 | ASTM D785 | |
| R-Scale | 119 | ISO 2039-2 | |
| Pencil Hardness 1 | 2H | JIS K5401 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2500 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 3 | 49.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/5 |
| Break 4 | 40.0 | MPa | ASTM D638 |
| Break | 42.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 5 | 18 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 6 | 2400 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 72.0 | MPa | ASTM D790 |
| -- 9 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 7.3 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 92 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 79 | J/m | ASTM D256 |
| 23°C 11 | 7.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 94.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 76.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 85.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | Condition: 500g |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.8 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Thickness: 4 mm |
| 11 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTATAL™ FV30 | Marplex Australia Pty. Ltd. | Acetal (POM) Homopolymer | ASTATAL™ |
| Estane® 58226 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Fainplast PVC RH 207/OP | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Kepital® F30-52G | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| TOLEN H030 GP/3 | SIBUR | PP Homopolymer | TOLEN |