CYCOLOY™ XCY620S resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XPiZnI_CYCOLOYXCY620Sresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ ABS automotive applications, excellent flow/impact balance, high heat resistance temperature and excellent properties retention after hydrolytic and heat aging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 260°C/5.0 kg | 20.0 | cm³/10min | ISO 1133 |
| 265°C/5.0 kg | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.30 | % | ISO 62 |
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.5 | % | ISO 527-2/50 |
| Fracture | 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 1 | 2300 | MPa | ASTM D790 |
| -- 2 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 82.0 | MPa | ISO 178 |
| Yield, 50.0mm span 3 | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | ||
| -30°C | 45 | kJ/m² | ISO 179/1eA |
| 23°C | 60 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | ||
| -30°C | No Break No Break | ISO 179/1eU | |
| 23°C | No Break No Break | ISO 179/1eU | |
| Notched Izod Impact 6 | ISO 180/1A | ||
| -30°C | 40 | kJ/m² | ISO 180/1A |
| 23°C | 55 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7 | ISO 180/1U | ||
| -30°C | No Break No Break | ISO 180/1U | |
| 23°C | No Break No Break | ISO 180/1U | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 65.0 | J | ASTM D3763 |
| 23°C, Total Energy | 55.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 128 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 8 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 108 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 106 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 129 | °C | ASTM D1525 10 |
| -- | 130 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C | Pass | IEC 60695-10-2 | |
| 100°C 11 | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 39 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 - 105 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 250 - 290 | °C | |
| Front Temperature | 250 - 290 | °C | |
| Nozzle Temperature | 240 - 280 | °C | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 sp=62mm |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| 10 . | 标准 B (120°C/h), 载荷2 (50N) |
| 11 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALSIN SE102 | Pooya Polymer Tehran | Polyolefin, Unspecified | CALSIN |
| Caltex PP MB71 | GS Caltex | PP, Unspecified | Caltex PP |
| Generic PMP | Generic | PMP | Generic |
| ISPLEN® PM 250 BX | REPSOL | PP Homopolymer | ISPLEN® |
| Karina IVORY PVC COMPOUND 880-35/ 1-F-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |