RTP 801 SI 2 DEL

Category: Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: XOo9FD_RTP-801-SI-2-DEL.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Glass Fiber Reinforced - Silicone Lubricated
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 10% filler by weight
Additive
  • Silicone lubricant (2%)
Features
  • Lubrication
RoHS Compliance
  • Contact manufacturer
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.46g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)1.2%ASTM D955
Moisture Content 0.15%
Additional InformationNominal ValueUnit
Primary Additive 10%
MechanicalNominal ValueUnitTest Method
Tensile Modulus 4480MPaASTM D638
Tensile Strength 68.9MPaASTM D638
Tensile Elongation (Yield)5.0 - 9.0%ASTM D638
Flexural Modulus 4140MPaASTM D790
Flexural Strength 110MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)64J/mASTM D256
Unnotched Izod Impact (3.20 mm)530J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)146°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating (1.50 mm, ** Values per RTP Company testing.)HBUL 94
InjectionNominal ValueUnit
Drying Temperature 121°C
Drying Time 2.0hr
Dew Point -31.7°C
Processing (Melt) Temp 182 - 218°C
Mold Temperature 79.4 - 107°C
Injection Pressure 68.9 - 103MPa
Injection instructions
Desiccant Type Dryer Required.
Resin Grade Manufacturer Category Trademark
Stamylex® 2H 280 Borealis AG HDPE Stamylex®
Geon™ BIO HC5185G PolyOne Corporation PVC, Flexible Geon™ BIO
Huafon JF-A-WV1008B Huafon Group Co., Ltd. PUR, Unspecified Huafon
Perflex TPE GP-50CE CP Chemie Resources (M) Sdn. Bhd. SEBS Perflex
OTECH ALLOY OE8021 - Profile OTECH Corporation TP, Unspecified OTECH ALLOY