LNP™ THERMOCOMP™ ZX08309 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XOLrgI_LNP-THERMOCOMP-ZX08309-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This material is mineral filled PPO grade with high dielectric constant and low loss tangent |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 | % | |
| Across Flow : 24 hr | 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 3200 to 3500 | MPa | ISO 178 |
| Flexural Strength 2(Break, 50.0 mm Span) | 90.0 to 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 134 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.10 GHz) | 4.40 to 4.60 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 2.0E-3 to 4.0E-3 | ASTM ES7-83 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 280 to 285 | °C | |
| Middle Temperature | 290 to 295 | °C | |
| Front Temperature | 300 to 305 | °C | |
| Nozzle Temperature | 290 to 295 | °C | |
| Processing (Melt) Temp | 295 to 305 | °C | |
| Mold Temperature | 90.0 | °C | |
| Back Pressure | 9.00 | MPa | |
| Screw Speed | 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 86-K268G-3 | Teknor Apex Company | PVC, Flexible | APEX® |
| Cheng Yu FV30715 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Petlon Prime B1-G15-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| Sylvin 2990-85 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| XENOY™ 1102 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |