Lupoy® 1200-08
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XMcVQT_Lupoy-1200-08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOY PC 1200-08 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C 1 | 60.0 | MPa | |
| Break | 72.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 150 | % | |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 96.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance - Change in Haze 2 | 45 | % | ASTM D1004 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C, 3.20 mm) | 900 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 | |
| Instrumented Dart Impact 4(23°C, 3.20 mm, Total Energy) | 89.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 4.00 mm | 144 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 128 | °C | |
| 1.8 MPa, Annealed, 4.00 mm | 141 | °C | |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 5 |
| Ball Indentation Temperature | > 125 | °C | IEC 60598-1 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.00 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 1.0E-3 | ASTM D150 | |
| Comparative Tracking Index (2.00 mm) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 0.500 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 2.50 mm | V-2 | ||
| 2.70 mm | V-2 | ||
| Glow Wire Ignition Temperature 6(2.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1000g, 500 cycles, CS-10F Wheel |
| 3 . | 0.25 mm Notch Depth |
| 4 . | 3.38 m/sec |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | 5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EPLAMID 66 CBR 15 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Karina BLACK PVC COMPOUND -E 650D48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KEBAFLOW® LCP HF140 | BARLOG plastics GmbH | LCP | KEBAFLOW® |
| LNP™ LUBRICOMP™ Lexan_LF1000 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |
| LONGLITE® PBT 6030-104X | CCP Group | PC+PBT | LONGLITE® PBT |