Mecoline S RDX 1203 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XLUiGV_Mecoline-S-RDX-1203-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Halogen-free, low smoke, highly oil and extra fuel resistant radiation cross-linkable, flame retardant compound for thin wall insulation of wire for Rolling Stock, Offshore and Marine/Aerospace applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 8.0 | g/10 min | ISO 1133 |
| Mooney Viscosity (ML 1+4, 150°C) | 29 | MU | DIN 53523 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 50 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 1 | 14.3 | MPa | |
| -- 2 | 9.00 | MPa | |
| Tensile Strain | IEC 811-1-1 | ||
| Break 3 | 170 | % | |
| Break 4 | 210 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 811-1-2 | ||
| 120°C, 240 hr | 21 | % | |
| 150°C, 168 hr | 24 | % | |
| Change in Tensile Strain at Break in Air | IEC 811-1-2 | ||
| 120°C, 240 hr | -16 | % | |
| 150°C, 168 hr | -20 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 5 | IEC 540 | ||
| Elongation under load | 15 | % | |
| Residual elongation | 5.0 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 165 to 185 | °C | |
| Extruder Screw L/D Ratio | 20.0:1.0 to 25.0:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 34 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 110 to 130 | °C | |
| Cylinder Zone 2 Temp. | 120 to 140 | °C | |
| Cylinder Zone 3 Temp. | 130 to 150 | °C | |
| Cylinder Zone 4 Temp. | 140 to 160 | °C | |
| Cylinder Zone 5 Temp. | 150 to 170 | °C | |
| Adapter Temperature | 155 to 175 | °C | |
| Die Temperature | 170 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | After crosslinking |
| 2 . | Before crosslinking |
| 3 . | After crosslinking |
| 4 . | Before crosslinking |
| 5 . | at 200°C/15min/0.2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ 1000H | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| AvaSpire® AV-848 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| EPO-TEK® OE188 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina BLACK PVC COMPOUND 795D48/1-B-IS-SD-GF (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BEIGE PVC COMPOUND 800-08/342-A-ERB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |