DINALEN® 55

Category:	LDPE , Low Density Polyethylene
Manufacturer:	DIOKI d.d.
Trademark:	DINALEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XLKS3K_DINALEN-55.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DINALEN® 55 is low density polyethylene containing slip and anti-blocking additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent.

DINALEN® 55 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film.

DINALEN® 55 is extruded at recommended melt temperature range between 160°C and 180°C. Recommended film thickness: 0.25 to 0.05mm.

Application

Thin slippery film of high gloss and transparency

Production of film for lamination

Production of film for a variety of primary flexible packaging like FFS for foodstuffs, sanitary articles, chemicals

Film production for a many kinds of carrier-bags, like airport security bags, DTK bags, cooler-bags, T-shirt-bags, shoulder-bags

Blending with DINALEN 50 to obtain a less slippery film

Mixing and co-extrusion with suitable i-polybutene-1 grades to produce film for peel systems

Mixing and co-extrusion with suitable polyolefin grades

General Information
Additive	Antiblock Slip
Features	Antiblocking High Clarity High Gloss Opticals Slip
Uses	Bags Blending Film Food Packaging Laminates Packaging
Agency Ratings	EC 1907/2006 (REACH) EU 2002/72/EC EU 2004/19/EC EU 94/62/EC
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Blown Film Coextrusion Film Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.923	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, Compression Molded)	45		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	200	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Yield, Compression Molded	11.0	MPa
Break, Compression Molded	15.0	MPa
Tensile Strain (Break, Compression Molded)	620	%	ISO 527-2
Coefficient of Friction			ISO 8295
vs. Itself - Dynamic	< 0.11
vs. Itself - Static	< 0.11

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Film Thickness - Recommended / Available	0.025mm to 0.050 mm
Tensile Strength			ISO 527-3
MD : 50 µm	20.0	MPa
TD : 50 µm	17.0	MPa
Tensile Elongation			ISO 527-3
MD : Break, 50 µm	220	%
TD : Break, 50 µm	330	%
Dart Drop Impact ¹(50 µm)	220	g	ISO 7765-1
Trouser Tear Resistance			ISO 6383-1
MD : 50 µm	90.0	N/mm
TD : 50 µm	80.0	N/mm

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	94.0	°C	ISO 306/A50
Melting Temperature	113	°C	ISO 11357-3

Optical	Nominal Value		Test Method
Gloss			ASTM D2457
20°, 50.0 µm	> 60
60°, 50.0 µm	> 110

Extrusion	Nominal Value	Unit
Melt Temperature	160 to 180	°C

Note Message
1 .	Profile 2

Resin Grade	Manufacturer	Category	Trademark
Sindustris POM FW701N	Sincerity Australia Pty Ltd.	Acetal (POM) Homopolymer	Sindustris POM
NEFTEKHIM PE 4116Q (16403)	Nizhnekamskneftekhim Inc.	LLDPE	NEFTEKHIM PE
LNP™ STAT-KON™ DE004 compound	SABIC Innovative Plastics	PC	LNP™ STAT-KON™
Lucofin® 1413	Lucobit AG	Polyolefin, Unspecified	Lucofin®
PENTAMID B GV35 H natur	PENTAC Polymer GmbH	Nylon 6	PENTAMID B