TECHNYL® C 246 NATURAL Datasheet,Nylon 6,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL® C 246 Natural is an unfilled polyamide 6, impact modified , for injection moulding. This grade offers high impact strength, flexibility and good surface aspect.

General Information
Additive	Impact modifier
Features	Impact resistance, high Low temperature impact resistance Good demoulding performance Excellent appearance
Uses	Large household appliances and small household appliances Power/other tools Industrial application Sporting goods Consumer goods application field
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Appearance	Natural color
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PA6

Physical	Dry	Conditioned	Unit	Test Method
Density	1.06	--	g/cm³	ISO 1183/A
Water Absorption (23°C, 24 hr)	1.2	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	1600	500	MPa	ISO 527-2/1A
Tensile Stress (Yield, 23°C)	38.0	34.0	MPa	ISO 527-2/1A
Flexural Modulus (23°C)	1550	400	MPa	ISO 178
Flexural Stress (23°C)	70.0	25.0	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	15	--	kJ/m²	ISO 179/1eA
23°C	82	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break	--		ISO 179/1eU
Notched Izod Impact (23°C)	80	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	60.0	--	°C	ISO 75-2/Af
Melting Temperature	222	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+14	1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+13	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	--	18	kV/mm	IEC 60243-1
Relative Permittivity	3.50	4.00		IEC 60250
Dissipation Factor	0.020	0.12		IEC 60250
Comparative Tracking Index (Solution A)	600	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.6 mm)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	230 - 235	°C
Middle Temperature	235 - 240	°C
Front Temperature	235 - 245	°C
Mold Temperature	60 - 80	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C.

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C.

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XLGtr0_TECHNYLC246NATURAL.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 2800 B-65A Z	RTP Company	TPO (POE)	RTP
Santron IMS1000	Bhansali Engineering Polymers Limited	SAN	Santron
Small Boss SPVC2004	Tongxiang Small Boss Special Plastic Products Co., Ltd.	PVC, Flexible	Small Boss
ADENE BHQBG	A.D. Compound spa	PP Copolymer	ADENE
Baoding 65E85	Baoding Bangtai Polymeric New-Materials Co.,Ltd	TPU-Polyester	Baoding