Diakon® CMG314V
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XKgAo6_Diakon-CMG314V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diakon®CMG314V is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion or injection molding. Diakon®The main characteristics of the CMG314V are: flame retardant/rated flame. Diakon®The typical application fields of CMG314V are: automobile industry |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 98 | ISO 2039-2 | |
| Ball Indentation Hardness | 185 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 2.0 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | 0.400 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 117 | °C | ISO 306/A |
| -- | 108 | °C | ISO 306/B |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 0.40 | % | ASTM D1003 |
| Additional Information |
|---|
| Mold Shrinkage, H 961/30: .4 to .7%.Craze Resistance (isopropanol), Ineos cantilever test: 600 secs to break. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-1000 | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| DENILUB PA66 NEAT RESIN | Vamp Tech | Nylon 66 | DENILUB |
| Diamond ABS 7500E | Network Polymers, Inc. | ABS | Diamond ABS |
| Honghai CM 352L | Weifang Honghai Plastics Technology Co., Ltd. | CPE | Honghai |
| Hifax TRC 779P HA 9B9 BLACK | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |