LNP™ STAT-KON™ AD000Z compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XHolLo_LNP-STAT-KON-AD000Z-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP Stat-Kon AD000Z is a compound based on ABS resin with carbon powder. Grade characteristics: a statically conductive extrusion grade. Also known as: LNP* STAT-KON* Compound A- E Product reorder name: AD000Z |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.28 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.41 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2780 | MPa | ASTM D638 |
| -- | 2690 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 41.0 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/5 |
| Break 3 | 37.0 | MPa | ASTM D638 |
| Break | 37.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 5 | 2.5 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4280 | MPa | ASTM D790 |
| -- 7 | 2570 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 34 | J/m | ASTM D256 |
| 23°C 8 | 4.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 9 | 23 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.90 | J | ASTM D3763 |
| 23°C, Total Energy | 3.90 | J | ASTM D3763 |
| -- | 1.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 96.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 84.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0 to 6.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® BMC 0400 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Silplus® 50 MP | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| TEPCON® M450 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | TEPCON® |
| Hytrel® 4068FG | DuPont Performance Polymers | TPC-ET | Hytrel® |
| PEARLSTICK® 46-10/06 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLSTICK® |