| PBT polyester natural reinforced with 50% of fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792 |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Ash Content | 48 to 52 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 16200 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 155 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus (23°C) | 14900 | MPa | ASTM D790 |
| Flexural Strength | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | °C | ASTM D648 |
| Melting Temperature 4 | 225 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Kingfa PBT G30 | Kingfa | PBT | Kingfa PBT |
| Hostacom G3 U01 102297 | LyondellBasell Industries | PP Copolymer | Hostacom |
| PENTAMID A MK30 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Hifax X4305 HL 86 C11287 | LyondellBasell Industries | PP Copolymer | Hifax |
| Kepital® FM2520S | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |