UMG ABS® 3001M
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | UMG ABS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XH3EZV_UMG-ABS-3001M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UMG ABS® 3001M is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of UMG ABS® 3001M are:
Typical application of UMG ABS® 3001M: Automotive |
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 42.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 27 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 81.0 | °C | ISO 75-2/Af |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 70.0 to 140 | MPa | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 5 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ C420CF | Mando Advanced Materials Co., Ltd. | LCP | SEPAZ™ |
| SLOVAMID® 66 BT LS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| TOTAL Polyethylene HDPE 5908 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| TyrFil® HD | Pathway Polymers | PUR-MDI | TyrFil® |
| Kumho PS HI 450PG | Korea Kumho Petrochemical Co., Ltd. | PS (HIPS) | Kumho PS |