LNP™ THERMOCOMP™ NX11302 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XG4wM9_LNP-THERMOCOMP-NX11302-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This is a PC/ABS compound with colorable, good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 | % | |
| Across Flow : 24 hr | 0.60 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.010 | % | |
| 24 hr, 50% RH | 0.010 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2350 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 47.0 | MPa | |
| Break | 46.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 4.6 | % | |
| Break | 75 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2230 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 50.0 mm Span | 79.0 | MPa | |
| Break, 50.0 mm Span | 78.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 106 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (1.00 GHz) | 2.94 | IEC 60250 | |
| Dissipation Factor (1.00 GHz) | 5.7E-3 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 96.1 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 199 to 249 | °C | |
| Middle Temperature | 216 to 254 | °C | |
| Front Temperature | 216 to 254 | °C | |
| Nozzle Temperature | 218 to 260 | °C | |
| Processing (Melt) Temp | 218 to 260 | °C | |
| Mold Temperature | 37.8 to 76.7 | °C | |
| Back Pressure | 0.517 to 0.862 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 72-D | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| SUPREME GPPS SC205 | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| NAXELL™ PC429HHI | MRC Polymers, Inc. | PC | NAXELL™ |
| NITRIFLEX NP-6000 | NITRIFLEX | NBR | NITRIFLEX |
| Karina IVORY PVC COMPOUND 602D35/ 1-C-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |