AVP™ TLL80CP
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XESxVs_AVP-TLL80CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVP™ TLL80CP is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength 1(Yield, 3.18 mm) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 75 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm, 50.8 mm Span) | 2410 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm, 50.8 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reverse Notch Izod Impact (23°C, 3.18 mm) | 2100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 127 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 16 | hr | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 288 | °C | |
| Nozzle Temperature | 266 to 282 | °C | |
| Processing (Melt) Temp | 271 to 288 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 10 SI 2 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| Synthos PS HI 945E | Synthos S.A. | PS (HIPS) | Synthos PS |
| AIE PP 80G6 | Asia International Enterprise (Hong Kong) Limited | PP, Unspecified | AIE PP |
| Osterlene® HB3553 | Osterman & Company | HDPE | Osterlene® |
| Sylvin 9067-80 Orange 586 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |