NORYL GTX™ GTX964 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XELG7z_NORYL-GTX-GTX964-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX964 is an unfilled impact modified material with optimised processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 1.4 - 1.8 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 80.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture | 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1800 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 20 | kJ/m² | ISO 180/1A |
| 23°C | 50 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(0.45 MPa, Unannealed, 100 mm Span) | 175 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | |||
| -- | 240 | °C | ISO 306/A50 |
| -- | 175 | °C | ISO 306/B50 |
| -- | 180 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 290 - 320 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | 290 - 320 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Karina IVORY PVC COMPOUND 750-35/1-B-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOTUF™ W1000I compound | SABIC Innovative Plastics Europe | PBT | LNP™ THERMOTUF™ |
| Plaslube® PA4/6 CF30 TL10 | Techmer Engineered Solutions | Nylon 46 | Plaslube® |
| EPIMAX® PC-900FVR | Osterman & Company | PC | EPIMAX® |
| TechnoPet GF 20 2 1 | TechnoCompound GmbH | PET | TechnoPet |