ELITE™ NG 5401B is a Linear Low Density Polyethylene, 1-Octene copolymer, produced with the SOLUTION™ technology. This resin presents excellent tensile, tear and puncture resistance even at low temperatures with great gloss and clarity. It has a low seal initiation temperature with high seal performance allowing an increase in the speed line of form, fill and seal. Main Characteristics
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | Internal method |
| Film Puncture Resistance | 9.02 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD | 132 | MPa | ASTM D882 |
| 2% secant, TD | 136 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 10.0 | MPa | ASTM D882 |
| TD : Yield | 10.0 | MPa | ASTM D882 |
| MD : Fracture | 38.0 | MPa | ASTM D882 |
| TD : Fracture | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 720 | % | ASTM D882 |
| TD : Fracture | 800 | % | ASTM D882 |
| Dart Drop Impact | 1000 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 680 | g | ASTM D1922 |
| TD | 890 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 62 | ASTM D2457 | |
| Haze | 11 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions for Blown Film: Screw Diameter: 63.5 mm (2.5 in); 24.5 L/D Type of Screw: Die Gap: 1.8 mm (70 mil) Melt Temperature: 232°C (450°F) Output: 52 kg/h (113 lb/h) Die Diameter: 152 mm (6 in) Blow-up Ratio: 2.5:1 Screw Speed: 83 rpm Frost Line Height: 635 mm (25 in) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V500MI20 | Lucent Polymers, Inc. | PP Homopolymer | Primefin |
| Sindustris PBT HV1006S | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| apinat® DP2165 | API SpA | Biodeg Polymers | apinat® |
| LEXAN™ FL910 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| POLIMAXX AN450R | IRPC Public Company Limited | ABS | POLIMAXX |