Electrafil® POM CO 13013 BK
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XDplXF_Electrafil-POM-CO-13013-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®POM CO 13013 BK is a polyoxymethylene (POM) copolymer product, which contains filler. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 3.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 60.7 | MPa | ASTM D638 |
| -- | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 99.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| Melting Temperature | 165 | °C | ASTM D785 |
| CLTE - Flow | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 - 1.0E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 - 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| TPCI # | 9962114 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 188 - 199 | °C | |
| Front Temperature | 182 - 193 | °C | |
| Nozzle Temperature | 177 - 188 | °C | |
| Processing (Melt) Temp | 188 - 204 | °C | |
| Mold Temperature | 76.7 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Drying not normally required. Dry at 180°F for 1 to 2 hours if necessary. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P50B07/P50B07-S (Single Strand) | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| TRAMID® 4110G40 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Elastron® G G100.A80.B.E | Elastron USA, Inc. | SEBS | Elastron® G |
| Hifax TYC 1123P E G14008 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Sylvin 3230-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |