| General purpose injection molding ASA with Visual Fx sparkle effect. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| -- | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 7.00 | cm³/10min | |
| 260°C/5.0 kg | 8.00 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.55 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1790 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 38.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2/50 |
| Break 3 | 30.0 | MPa | ASTM D638 |
| Break | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 2.5 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2/50 |
| Break 5 | 4.0 | % | ASTM D638 |
| Break | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1790 | MPa | ASTM D790 |
| -- 7 | 1900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 50.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 55.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 56 | J/m | ASTM D256 |
| 23°C | 130 | J/m | ASTM D256 |
| -30°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 12 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 17.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 100 mm Span 12 | 88.0 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 77.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 13 | 75.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ASTM D1525 14 |
| -- | 86.0 | °C | ISO 306/B50 |
| -- | 91.0 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 8.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 210 to 240 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 15S3304 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| RTP 4085 TFE 15 SI 2 | RTP Company | PPA | RTP |
| TPC PVC SG71J | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| LNP™ THERMOCOMP™ RZ006 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| POLYfill PPHC K2040H | Polykemi AB | PP, Unspecified | POLYfill |