SCARAB SB
| Category: | Urea Formald , Urea Formaldehyde |
| Manufacturer: | BIP (Oldbury) Limited |
| Trademark: | SCARAB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XDC16I_SCARAB-SB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low cost material available in black and brown suitable for a wide range of applications, particularly Electrical and Closures |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Apparent Density | 0.66 | g/cm³ | ISO 60 |
| Bulk Factor | 2.3 | ISO 171 | |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.74 | % | |
| -- 2 | 0.80 | % | |
| Water Absorption | |||
| Cold 3 | 180.0 | mg | DIN 53472 |
| Cold 4 | 57.0 | mg | ISO 62 |
| Hot 5 | 280.0 | mg | ISO 62 |
| Post Shrinkage | ISO 2577 | ||
| -- 6 | 0.50 | % | |
| -- 7 | 0.44 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 120 | °C | DIN 43458 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 2.0 | kJ/m² | ISO 180/C |
| Unnotched Izod Impact Strength | 8.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 138 | °C | ISO 75-2/Ae |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | DIN 53483 |
| Volume Resistivity | 1.0E+12 | ohms·cm | DIN 53483 |
| Electric Strength | IEC 60243-1 | ||
| -- 8 | 7.8 | kV/mm | |
| -- 9 | 6.2 | kV/mm | |
| Dissipation Factor | 0.034 | DIN 53483 | |
| Comparative Tracking Index | > 600 | V | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Oxygen Index 10 | 33 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Preheated powder |
| 2 . | Cold powder |
| 3 . | 96 hr @ 23°C |
| 4 . | 24 hr @ 23°C |
| 5 . | 30 min @ 100°C |
| 6 . | Cold powder |
| 7 . | (48 hr) Preheated powder |
| 8 . | (90°C) Preheated powder |
| 9 . | Cold powder |
| 10 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600/42 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Daelim Po1y® LH-4100 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| ExTima™ GP MB LCP 530 | Ovation Polymers Inc. | LCP | ExTima™ |
| Electrafil® PA6 04001 FR MB | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| POLYBEST 6 PD GF30 natural | POLYMA Kunststoff GmbH & Co. KG | Nylon 6 | POLYBEST |