Edgetek™ CY4000 L BK025
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XD53ok_Edgetek-CY4000-L-BK025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified PC/PBT alloy with outstanding impact strength and chemical resistance |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage (3.00 mm) | 0.40 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 61.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2300 | MPa | ASTM D790 |
| Flexural Strength 3 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V903 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| KOPELEN J-330S | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| LNP™ LUBRICOMP™ RAL22I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Sylvin 8215-82 Purple 8424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| EPALINE 386A51 | Epaflex Polyurethanes S.R.L. | TPU, Unspecified | EPALINE |