INEOS PP L25Zh00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XCuluq_INEOS-PP-L25Zh00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| L25Zh00 is an ultra-high melt flow rate, nucleated, antistatic and lubricated impact copolymer polypropylene designed for an optimum balance of stiffness and impact resistance required for high-speed, thin-walled injection molding, and high length-to-thickness ratio rigid packaging applications. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 130 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 29.4 | MPa | |
| Break | 24.1 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.4 | % | |
| Break | 18 | % | |
| Flexural Modulus - 1% Secant | 1390 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 34 | J/m | |
| 23°C | 60 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 3.34 | kJ/m² | |
| 23°C | 5.94 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Brittle | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 112 | °C | |
| 1.8 MPa, Unannealed | 58.1 | °C | |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 74 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas SER20 | PlastxWorld Inc. | ABS | Veroplas |
| Nipol® NBR N1201 | Zeon Corporation | NBR | Nipol® NBR |
| Latigray 52/11-01 CX/45 | LATI S.p.A. | PP Homopolymer | Latigray |
| InnoTuf® TP-4054 | Innovative Polymers, Inc. | TSU | InnoTuf® |
| Plaslube® PA6 ML2 HS BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |