LNP™ LUBRICOMP™ UCL16AS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XAwhas_LNP-LUBRICOMP-UCL16AS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Internally lubricated Polyphtalamide compound, containing Carbon Fiber and PTFE. Added features include Heat Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 272 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19000 | MPa | ISO 178 |
| Flexural Stress | 373 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.0E-6 | cm/cm/°C | |
| Transverse : 23 to 60°C | 4.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2277 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| RONFALIN® STA32 | A. Schulman Europe | ABS | RONFALIN® |
| TOTAL Polyethylene XSene® HDPE XRC20 Blue | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| XENOY™ X5230 resin | SABIC Innovative Plastics Europe | PC+PET | XENOY™ |
| Sylvin 86006-70FU Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |