Ultramid® A3U40G5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XALGmU_Ultramid-A3U40G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Without halogenes flame retarded glass fiber reinforced injection moulding grade; light colorable; outstanding mechanical and electrical properties. In particular optimized for the glow wire requirements of IEC 60335. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 30.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 1.1 | -- | % | ISO 294-4 |
| Flow direction | 0.40 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.7 - 5.1 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.4 - 1.6 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 140 | -- | cm³/g | ISO 307 |
| Mold shrinkage- model-housing (1.50 mm) | 0.40 - 0.60 | -- | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Smoke Toxicity - CIT NLP acc. to CEN/TS 45545-2 | 0.410 | -- | NF X70-100 | |
| Smoke density- Ds max. (20 min), 25kW/m², 2mm | 100 | -- | ISO 5659-2 |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA66-GF25 FR | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | 3.8 | % | ISO 527-2 |
| Flexural Modulus | 9800 | 7500 | MPa | ISO 178 |
| Flexural Stress | 220 | 170 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | 4.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.017 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | V-0 | -- | UL 94 | |
| 0.800 mm | V-0 | -- | UL 94 | |
| 1.60 mm | 5VA | -- | UL 94 | |
| Glow Wire Flammability Index (> 0.750 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (> 0.750 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 290 | °C | |
| Middle Temperature | 290 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx F663E43 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| TEKALOY™ G70A2 | Mando Advanced Materials Co., Ltd. | PC+ABS | TEKALOY™ |
| NEOFLON™ AP-231SH | DAIKIN AMERICA, INC. | PFA | NEOFLON™ |
| CP PRYME® Polypropylene PPC100NB-.8FM | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| EnCom F0 PC20GF | EnCom, Inc. | PC | EnCom |