Order Products : sales@su-jiao.com
FORMULA P ELAN 6003 UV
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X9FKlk_FORMULA-P-ELAN-6003-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FORMULA P ELAN 6003 UV is a polypropylene product,. It is available in Europe. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 - 1.7 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 | MPa | ISO 527-2 |
| Fracture | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 500 | % | ISO 527-2 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 44.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 7.0 | kJ/m² | ISO 180 |
| 23°C | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 63.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 22 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201D UV | RTP Company | Nylon 612 | RTP |
| VYPET VNT 930 | Lavergne Group | PET | VYPET |
| NEFTEKHIM PP 1502H (S30S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| CEPLA CW-452K | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| Epocast 1626 A/B | Huntsman Advanced Materials | Epoxy | Epocast |