EL-Lene™ H1000PBL
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X8ZQnX_EL-Lene-H1000PBL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H1000PBL is a blue, bimodal, high density polyethylene compound that is specially designed for water pressure pipe, especially for drinking water pipes. EL-Lene H1000PBL is designed as PE100 pipes providing excellent in mechanical properties, and processablitiy. Well dispersed UV stabilizer and anti-oxidant which also provide outstanding UV resistance and high thermal stability for long term using. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.28 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F0) | > 10000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/100 | ||
| Yield | 23.0 | MPa | |
| Break | 36.0 | MPa | |
| Tensile Strain (Break) | 850 | % | ISO 527-2/100 |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Resistance to Slow Crack Growth (80°C) | > 1000 | hr | ISO 13479 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 50 | min | ISO 10837 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Minimum Required Strength | 10.0 | MPa | ISO 9080 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 200 | J/m | |
| 0°C | 260 | J/m | |
| 23°C | 300 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6300HD | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Next Nylon 66 Prime Series PG15-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Lucent PP PPC-220 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| SEQUEL® 1580-UV 598F ANTHRACITE | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Sylvin 4200-68 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |