GAPEX® RPP20EA HB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X7NF8q_GAPEX-RPP20EA-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX® RPP20EA HB is a Polypropylene material filled with 20% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Important attributes of GAPEX® RPP20EA HB are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 45.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 2850 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 0.226 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 149 | °C | |
| 1.8 MPa, Unannealed | 127 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 221 to 238 | °C | |
| Middle Temperature | 227 to 243 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Nozzle Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 221 to 238 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 to 0.345 | MPa | |
| Cushion | 5.08 to 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas E11 | PlastxWorld Inc. | ABS | Veroplas |
| Boda BDF-H2902 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Europrene® 1500 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| Fainplast PVC GK 80/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| IDI BMC 6060D | IDI Composites International | TS, Unspecified | IDI BMC |