DAI-EL™ LT-252
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | DAI-EL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X6xFc7_DAIELLT252.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DAI-EL LT-252 is a fluoroelastomer which can be cured by peroxide whose cold temperature resistance, a drawback of conventional fluoroelastomer, has been improved. It offers excellent mechanical properties, and bending and acid resistance, etc. The TR10 of this material is -25°C, providing excellent low-temperature sealing performance and solvent resistance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.86 | g/cm³ | JIS K6268 |
| Mooney Viscosity (ML 1+10, 100°C) | 40 | MU | JIS K6300-1 |
| Fluorine Content | 66.5 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 66 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 2.60 | MPa | JIS K6251 |
| Tensile Strength | 17.4 | MPa | JIS K6251 |
| Tensile Elongation (Break) | 260 | % | JIS K6251 |
| Compression Set 2(200°C, 70 hr) | 29 | % |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 25% compression |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adiprene® LW 520 | Chemtura | PUR-Eth,aliphat | Adiprene® |
| Fibremod™ GE225U | Borealis AG | TPO | Fibremod™ |
| FRIANYL® A3 GF30 V0 | Nilit Plastics | Nylon 66 | FRIANYL® |
| Stat-Tech™ PA66 C20 black (EM00000364BI) | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| 3M™ Dyneon™ TFM™ Modified PTFE TFMR 1602 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |