Multi-Flex® TPE A1540
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | Multi-Flex® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X5Ylt0_Multi-Flex-TPE-A1540.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Multi-Flex® TPE A1540 is a Thermoplastic Elastomer (TPE) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: good uv resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 15 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 2.42 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 870 | % | ASTM D412 |
| Tear Strength | 11.4 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 160 | °C | |
| Middle Temperature | 168 | °C | |
| Front Temperature | 177 | °C | |
| Nozzle Temperature | 177 | °C | |
| Processing (Melt) Temp | 177 | °C | |
| Mold Temperature | 26.7 to 32.2 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V74C | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Spartech Polycom PP5430 | Spartech Polycom | PP, Unspecified | Spartech |
| DeWAL DW 216 | DeWAL Industries | PTFE | DeWAL |
| Hetron™ FR 1540 | Ashland Performance Materials | Vinyl Ester | Hetron™ |
| POCAN® B 3235 POS151 000000 | LANXESS GmbH | PBT | POCAN® |