INSULCAST® 985 FR
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X5Ch4a_INSULCAST-985-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 985 FR is a semi-flexible flame retardant epoxy compound displaying the best thermal shock resistance currently available in an epoxy compound. It has excellent electrical properties over a wide range of temperatures and conforms to the component program of Underwriters Laboratories' Flame Class 94V-O. INSULCAST 985 FR makes use of the latest polymer and filler technology. |
| General Information | |
|---|---|
| Features |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 3.2E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.43 to 0.58 | W/m/K | |
| Service Temperature | -55 to 155 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Shock Resistance - Method 107E 1 | Passes B-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.030 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Black | ||
| -- 3 | Colorless | ||
| Density | |||
| -- 4 | 1.50 | g/cm³ | |
| -- 5 | 1.62 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 6 | 18 | Pa·s | |
| 25°C 7 | 50 | Pa·s | |
| -- 8 | 80 | Pa·s | |
| Curing Time | |||
| 125°C | 2.0 | hr | |
| 85°C | 16 | hr | |
| Pot Life (25°C) | 240 to 360 | min |
| Note Message | |
|---|---|
| 1 . | MIL STD 202 |
| 2 . | Part A |
| 3 . | Part B |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | Part A |
| 7 . | Mixed |
| 8 . | Part B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trithene® TU 3001 | Petroquimica Triunfo | LDPE | Trithene® |
| APEX® 94-A0098C-85 | Teknor Apex Company | PVC, Flexible | APEX® |
| Clariant PC PC-1100TF15 | Clariant Corporation | PC | Clariant PC |
| LUVOCOM® 1105-8487 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| PLEXIGLAS® Film 0F016 | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |