Kingfa FRHIPS-113
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X53IwH_Kingfa-FRHIPS-113.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa FRHIPS-113 is a High Impact Polystyrene material. It is available in Asia Pacific or North America. Important attributes of Kingfa FRHIPS-113 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 45 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 2200 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COSMOTHENE® L705 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® |
| GAPEX® RPP30EA20HB-BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| PLEXIGLAS® Film 0F016 | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |
| Sylvin 8354-62D Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTOPLAST XU 435BB11 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |