Order Products : sales@su-jiao.com
CERTENE™ LLI-2024
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X4BGHT_CERTENELLI2024.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLI-2024 is a certified prime resin specially designed for injection molding applications requiring good low temperature resistance and low warpage. LLI-2024 features easy processability over a wide range of molding conditions. LLI-2024 applications include housewares, closures, caps, medical parts, and toys where toughness, high impact resistance and high gloss are required. Recommended processing temperature is180 to 220°C., with mold at 20 to 40°C. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, Compression Molded, F50) | 19.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 12.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 500 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Compression Molded) | 448 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 71.5 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -90.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTALAC™ ASA 314 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| Fiberfil® M-1492 BK223 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Elexar® EL-1934E | Teknor Apex Company | TPE | Elexar® |
| Hifax TRC 221X 3001 | LyondellBasell Industries | PP Copolymer | Hifax |
| TAFMER™ XM-5080 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |