Grilamid® TRVX-50X9 nat
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X3W5Ex_Grilamid-TRVX-50X9-nat.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid® TRVX-50X9 nat is a Polyamide 12 (Nylon 12) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Grilamid® TRVX-50X9 nat: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.10 | -- | % | |
| Flow | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 1.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | -- | 190 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | -- | 12500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | -- | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | -- | 2.1 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | -- | 15 | kJ/m² | |
| 23°C | -- | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | -- | 60 | kJ/m² | |
| 23°C | -- | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 115 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 105 | -- | °C | ISO 75-2/C |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 80.0 to 110 | -- | °C | |
| -- 2 | 120 | -- | °C | |
| Glass Transition Temperature 3 | 125 | -- | °C | ISO 11357-2 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 8.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA MACM12+X, MH, 12-120, GF50 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CERTENE™ PHE35 | Muehlstein | PP Homopolymer | CERTENE™ |
| DENKA EVA TEX 81 | Denka Company Limited | EVA | DENKA EVA TEX |
| K-Flex 3350 | Technovinyl Polymers India Ltd. | PVC Elastomer | K-Flex |
| Lusin® Alro OL 141 | Chem-Trend L.P. | Unspecified | Lusin® |
| SQUARE® LSG6933-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |