LEXAN™ DMX2415 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X36oQz_LEXAN-DMX2415-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This product will be phased out per January 2015 -- LEXAN DMX2415 is a polycarbonate resin with improved scratch resistance. LEXAN DMX2415 is available in transparent, translucent, and opaque colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183, ASTM D792 |
| Specific Volume | 0.850 | cm³/g | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Erichson Scratch Depth - 6N | 14.0 | µm | Internal Method |
| Pencil Hardness 1 | H | ASTM D3363 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 13.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | Internal Method |
| Water Absorption | |||
| 24 hr | 0.080 | % | ASTM D570 |
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Saturation, 23°C | 0.27 | % | ISO 62 |
| Equilibrium, 23°C | 0.28 | % | ASTM D570 |
| Equilibrium, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| L-Scale | 108 | ||
| M-Scale | 93 | ||
| Ball Indentation Hardness (H 358/30) | 128 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2900 | MPa | ASTM D638 |
| -- | 2450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 80.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/50 |
| Break 4 | 65.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Break 6 | 70 | % | ASTM D638 |
| Break | 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2600 | MPa | ASTM D790 |
| -- 8 | 2450 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 108 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 120 | MPa | ASTM D790 |
| Taber Abrasion Resistance | |||
| 1000 Cycles, 1000 g, CS-17 Wheel | 10.0 | mg | Internal Method |
| 1000 Cycles, 1000 g, CS-17 Wheel | 10.0 | mg | ASTM D1044 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (23°C) | 200000 | cm³·mm/m²/atm/24 hr | ASTM F1307 |
| Water Vapor Transmission Rate (38°C, 100% RH) | 0.90 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | 47 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 30 | J/m | ASTM D256 |
| 23°C | 30 | J/m | ASTM D256 |
| -30°C 12 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| -30°C 14 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 133 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 15 | 131 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 119 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 16 | 118 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 139 | °C | ASTM D1525 17 |
| -- | 138 | °C | ISO 306/B50 |
| -- | 140 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 140°C 18 | Pass | ||
| CLTE | |||
| Flow : -40 to 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1400 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.90 | ||
| 60 Hz | 2.90 | ||
| 1 MHz | 2.80 | ||
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.584 | ASTM D542, ISO 489 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 280 to 305 | °C | |
| Front Temperature | 295 to 315 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Processing (Melt) Temp | 295 to 315 | °C | |
| Mold Temperature | 70.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1 kgf |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 80*10*4 mm |
| 16 . | 80*10*4 mm |
| 17 . | Rate B (120°C/h), Loading 2 (50 N) |
| 18 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synthos EPS® 2040F/CZ | Synthos S.A. | PS (EPS) | Synthos EPS® |
| Toraycon® 1201G-15 | Toray Resin Company | PBT | Toraycon® |
| Karina NATURAL PVC COMPOUND 800-25/ 1-AYR-IS-LMP (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lotrène® LDPE FE3000 | QAPCO | LDPE | Lotrène® LDPE |
| PermaStat® 105 | RTP Company | PP, Unspecified | PermaStat® |